I believe that everyone has a certain understanding of refractory materials. Today, Zhengzhou sunrise refractory materials will introduce you to the application of refractory materials in different parts of the glass furnace.
 
(1) Side wall
An ideal refractory material is placed in the sodium-calcium-silica glass furnace and the boron glass furnace to fuse the sidewalls of the AZS block. It contains 33-41% ZrO2. In the alkali-free glass or low-alkali glass fiber kiln, the side walls are all built with AZS bricks or dense zirconium bricks or fused silica bricks.

(2) bottom
The bricks at the bottom are required to have good wear resistance and good integrity. The bottom is now usually a multi-layer composite structure. The main layer of the multilayer structure is the layer of large fire clay bricks. The protective layer and the wear layer are laid on the fired clay bricks. The protective layer is made of zirconium lanthanum or AZS. The wear layer is laid over the protective layer to protect the bottom of the crucible and in direct contact with the molten glass. It is usually built with AZS bricks with good corrosion resistance and wear resistance. This composite bottom structure reduces heat loss and extends furnace life. In the case where the molten glass contains heavy elements (such as lead glass) or heavily corrosive glass (such as opal glass), in order to prevent leakage, another protective layer and a wear layer and a wear layer on the original protective layer are added. The original protective layer and wear layer are also secondary paving processes and can be constructed with sintered AZS bricks or zirconium bricks.
(3) Feeding pool
The feed cell brick is corroded by powder and molten glass. The erosion of the powder, the scouring of the molten glass and the effect of the flame all do damage to the brick, so the corrosion resistance is serious. Casting AZS 41#WS is used and thickened in this section, air cooled. In addition to the bricks in the corner, AZS 33# is built in other areas. The bottom feed pool is constructed with large cast kaolin bricks.

(4) Throat
The flow of molten glass in the throat is the largest. And there is obvious convection. These accelerate erosion. Therefore, the throat covering tiles are built with AZS 41#. The side wall bricks of the throat are constructed of the same material as the cover brick, at least the WS brick. Silicon silicate glass is used when molten.

(5) cooling the tank and forming a tank
The molten glass is refined in a cooling tank and a forming tank. It has entered the post-melting process. At this time, you should avoid any defects that contain bubbles, streaks and stones. The cooling bath is built with AZS 33# manufactured by an oxidation process. The glass phase has a high bleed temperature and does not generate bubbles. In the formation of the groove should be constructed with α-β fused cast alumina block ORα fused cast alumina block.
上一篇:Guidelines for the selection of refractories for glass kiln 下一篇:What kind of refractory materials can be divided into?
Product List
Contact Us

Email:sales@sunriserefr.com

MSN:hksunrise@hotmail.com

Skype:tkfanyi zzty371

Whatsapp:+86-13598430175

Mobile:+86-13015506292

Tel: +86-371-63838939

Fax: +86-371-63835539

Inquiry
Name:
Tel:
Email:
Message: