The mineral composition of refractory brick is mainly kaolinite (Al2O3 · 2SiO2 · 2H2O) and 6% ~ 7% impurities (potassium, sodium, calcium, titanium, iron oxide). Select the high density, low water

absorption of raw material, a reasonable level of preparation is the key to make low porosity refractory brick. Glass mould brick is made with 50% soft clay and 50% hard clay clinker according to

certain granularity requirements. After molding and drying,  firing under high temperature of 1300 ~ 1400 ℃.






The firing process is mainly due to the process of crystallization of mullite (3Al2O3 · 2SiO2). The SiO2 and Al2O3 in the refractory brick form a eutectic and low melting point silicate with the impurity

during the firing process, surrounded by mullite crystals. The maximum temperature in the firing process is usually controlled at 1350 ° C to 1380 ° C, and the firing temperature of the low porosity

fire clay brick (1420 ° C) is increased. The shrinkage of refractory brick is slightly increased, so that the density of refractory material increases slightly and the low porosity is decline.

Refractory brick do not use the same kind of mud to use different appliances, fire mud selection of cleaning water, accurate weighing modulation, uniform mixing, tune the mud can not be

arbitrarily diluted with water, mortar fullness is greater than 95% or more, ensure solid brick joints, the surface brick seam jointing with virgin pulp, the shell can not correct the parts with mud.
上一篇:The trends in the refractory development 下一篇:Development trend of refractory industry in the future
Product List
Contact Us

Email:sales@sunriserefr.com

MSN:hksunrise@hotmail.com

Skype:tkfanyi zzty371

Whatsapp:+86-13598430175

Mobile:+86-13015506292

Tel: +86-371-63838939

Fax: +86-371-63835539

Inquiry
Name:
Tel:
Email:
Message: